cast bullet weight tolerance question

[powderburner]

nope , just about right ,, I meant the mould wasn't quite up to temp when you started, and when you were casting the heavier ones your cadence speeded up a little ,it sounds like though that you have it mostly in hand ,,, you do not say how many on the low end and how many on the high, at 421 .9 and 422 you were pouring smooth and maintaining an even mould temp.You get variances no matter how you do it other than weigh each one as it is dropped and reject all that are not to your spec,