[beltfed]

Kurt,
You don't have to be sorry about that. THanks for posting that picture.
The hardness of my 9+1 COWW/Lino is about 15+ or so on the Lee and Saeco testers.
Re. trying harder alloy: That old WW stash you have should have a higher amount of antimony
than the latest WWs. Little or no tin.
I came up with the Lino addition because I could. Have pretty good supply of it.
I have also found that you can make up a pretty hard alloy with the (especially older) WW
by simply adding about 1-1.5% tin to make it cast better.
Meanwhile, I think there is going to be a heavy little care pkg for you at Rapids...
I am always happy to share what I can- info and other stuff to help others
in the shooting sports.